The tufted belt of 32T is a substitute product for TPV flocking based on the production process and technical requirements of the automobile seal industry. Use of TPV note when it is squeezed waste heat (180-210 ° C), the ribbon of the flock will be a good fit in the section of need flocking. The product fitting process is simple, the production stability is good, the construction investment is small, the sealing part enterprise brings environmental protection, the integrated cost of the product drops. The performance index is stable, decorative wear-resisting and so on.

 

1, features

The joints are less, the process is simple, the stability is good, the elimination of the different sound, the soft wear-resisting is excellent.

 

2, performance

Ordinal number

Test item

Testing standard

Determine the calibration

1

Thermal aging

1、GM9131P-1994: 80±2°C×240h
2. After 24h at room temperature, wear resistance after standard gm-9909-2004

5000 times of wear-resisting can not see the base material, in the detection surface should have thin and even the flocking face, the velvet belt has no crack, the base material has no obvious bending, no damage.

2

High temperature resistance

1、GM9329P-2003: 80±2°C,95±5% humidity ×240h。
2. After 24h at room temperature, wear resistance after standard gm9909p-2004

5000 times of wear-resisting can not see the base material, in the detection surface should have thin and even the flocking face, the velvet belt has no crack, the base material has no obvious bending, no damage.

3

Heat cycle

1, 80 + 2 ° C x 15.5 h at room temperature 15.5 h - 30 + 2 ° C x 7.5 h at room temperature for 0.5 h50 plus or minus 2 ° C and 95 + / - 5% humidity room temperature is 0.5 x 15.5 h h - 30 + 2 ° C x 7.5 h at room temperature for 0.5 h, the above cycle 5 times.
2. After 24h at room temperature, wear resistance after standard gm9909p-2004

5000 times of wear-resisting can not see the base material, in the detection surface should have thin and even the flocking face, the velvet belt has no crack, the base material has no obvious bending, no damage.

4

The friction resistance

PV3363-2006

Load 250G, travel 70mm. Speed 60 plus or minus 5 reciprocating/min. After 250 times, the rubber layer is in good condition, and the base material can not be found. On the test surface, it should have a thin and uniform flocking surface

5

Wear resistance

GM9909-2004

Standard or room temperature environment, load 1kh, cycle wear-resisting 10,000 times invisible base material, should have thin and uniform flocking surface on the detection surface

6

Xenon aging

Gm9909p-2004, SAEJ2527-2004 (500KJ/square) aged 1KG with 5000 friction loads

On the detection surface should have thin and uniform flocking surface, the velvet belt has no crack, no obvious bending of the base material, no damage.

7

The most energetically N

ASTM D412-06a2013

Velvet strip ≥18N   Stretch speed: 500mm/min raw distance: 25mm

Next:22T series
inquiry

Wenzhou Qi Wang Flocking Co.,Ltd.

Add: No. 158, Zhenqian Road, Lupu Town, Cangnan Village Zhejiang
Hotline: +86-577-64452111
Service: 400-072-8898
Fox: +86-577-64452000

Copyright© Wenzhou Qi Wang Flocking Co.,Ltd. All Rights Reserved.

Message

workday:7:30-17:00
weekend:7:30-17:00

OPEN

Message

Please leave a message

*

Title

*

Name

*

Tel

*

Email

*